ORIGINAL ARTICLE
Year : 2022  |  Volume : 25  |  Issue : 12  |  Page : 2024-2029

Evaluation of the effect of anodization-colored titanium abutments and zirconia substructure thickness on zirconia substructure color: An In vitro study


1 Department of Prosthodontics, Institute of Health Sciences, Istanbul Medipol University, Istanbul, Turkey
2 Department of Prosthodontics, Faculty of Dentistry, Istanbul Health and Technology University, Istanbul, Turkey

Correspondence Address:
Mr. B B Bas
Cibali, Atatürk Blv., Fatih, Istanbul
Turkey
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/njcp.njcp_484_22

Rights and Permissions

Background and Aim: The aim of this study is to evaluate the effect of anodized titanium abutments and zirconia substructure thickness on the color of zirconia substructure. Materials and Methods: In this study, an electrochemical anodization setup was prepared for titanium coloring. Commercial titanium, anodization-colored yellow and pink titanium, and zirconia were used as different abutment specimens. Thirty zirconia discs in 0.7, 0.9, and 1.1 mm thickness were prepared from zirconia blocks as zirconia substructure specimens (n = 10). Zirconia substructure specimens of different thicknesses were placed on abutment specimens of different colors and L*, a*, b* values were measured with a spectrophotometer device. Color difference (ΔE) was calculated according to the CIELab formula by comparing the L*, a*, and b* values obtained on the zirconia abutment with the L*, a*, and b* values obtained on the other abutments. Statistical analyzes were performed with two-way analysis of variance and Tukey Honestly Significant Difference (HSD)test (p < 0.05). Results: The increase in the thickness of the substructure resulted in a statistically significant difference on ΔE, L*, a*, and b* values (p < 0.001). The effect of abutment color had no significant effect on ΔE values. The highest ΔE value was 18.10 at zirconia substructure with 0.7 mm thickness when paired with pink-anodized titanium abutment specimens. Conclusion: The thickness of zirconia substructure and the color of titanium abutments affect zirconia substructure color.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed192    
    Printed10    
    Emailed0    
    PDF Downloaded25    
    Comments [Add]    

Recommend this journal