The effects of disinfection with Er, Cr:YSGG laser, application of CPP–ACP and sodium hypochlorite on shear bond strength


Department of Paediatric Dentistry, Cukurova University, Adana, Turkey

Correspondence Address:
Dr. I Yazicioglu
Cukurova University, Dis Hekimligi Fak, Pedodonti AbD, Balcalı, Saricam, ADANA
Turkey
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/njcp.njcp_1594_21

Rights and Permissions

Background: The effects of commonly used antimicrobial and anticariogenic agents on the adhesion of pit and fissure sealants were investigated in this study. Aims: The aim of this study is to evaluate the effects of erbium, chromium: yttrium-scandium-gallium-garnet (Er, Cr:YSGG) laser disinfection, casein phosphopeptides–amorphous calcium phosphate (CPP–ACP) containing paste and sodium hypochlorite application before the placement of a resin-based pit and fissure sealant on the shear bond strength of primary tooth enamel. Materials and Methods: The shear bond strength test evaluated the bond strength of sealants on the buccal enamel surfaces of primary molar teeth. The study groups were pit and fissure sealant without any preapplication, pre application of disinfection with Er, Cr:YSGG laser, disinfection with Er, Cr:YSGG laser and CPP–ACP containing paste, sodium hypochlorite, sodium hypochlorite and CPP–ACP containing paste and CPP–ACP containing paste. The pit and fissure sealants were placed using 4 mm diameter, 2 mm height cylindrical plastic tubes. Shear force was applied to each sample. The surfaces of the broken samples were detected under stereomicroscope and were grouped as adhesive, cohesive, and mixed. The results of the study were evaluated using the SPSS 16.0 package program for statistical analysis Results: The groups where sodium hypochlorite and sodium hypochlorite with CPP-ACP were applied showed the lowest bond strength (p < 0.05). It was observed that most of the failures in these groups were adhesive-type failures. No significant difference was observed between the shear bond strengths of the other groups (p < 0.05). Conclusions: Er, Cr: YSGG laser and CPP-ACP containing paste are alternative methods for pre-application of fissure sealants.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed922    
    Printed20    
    Emailed0    
    PDF Downloaded278    
    Comments [Add]    

Recommend this journal